作者:D. Krastev , V. Pauno , B. Yordanov
来源:[J].Fracture and Structural Integrity, 2016, Vol.10 (37), pp.280 - 286Gruppo Italiano Frattura
摘要:In this work are discussed some experimental data about the obtaining of recast layers on the surface of high speed tool steel after electrical discharge treatment in electrolyte. The electrical discharge treatment of steel surface in electrolyte produces a recast layer with spec...
作者:Ermioni D. Pasiou , D. Triantis
来源:[J].Fracture and Structural Integrity, 2017, Vol.11 (40), pp.41 - 51Gruppo Italiano Frattura
摘要:An experimental protocol is described including a series of uniaxial compression tests of three brittle materials (marble, mortar and glass). The Acoustic Emission (AE) technique and the Pressure Stimulated Currents (PSC) one are used since the recordings of both techniques are s...
作者:D. Nowell , K I. Dragnevski , S J. O�Connor
来源:[J].Fracture and Structural Integrity, 2017, Vol.11 (41), pp.197 - 202Gruppo Italiano Frattura
摘要:This paper introduces the use of digital image correlation for the measurement of surface displacements in the neighbourhood of a crack tip, both at the macro- and micro- scale. Various methods of interpreting the measured data and producing a crack driving force are then discuss...
作者:D. Rozumek , S. Faszynka
来源:[J].Fracture and Structural Integrity, 2017, Vol.11 (42), pp.23 - 29Gruppo Italiano Frattura
摘要:The paper presents the results of tests on the fatigue crack growth for a constant moment amplitude under combined bending with torsion in the aluminium alloy AW-2017A-T4. The tests were performed under different values of the load ratio R. Plane specimens with stress concentrato...
作者:D. Rozumek , Z. Marciniak
来源:[J].Fracture and Structural Integrity, 2017, Vol.11 (42), pp.40 - 45Gruppo Italiano Frattura
摘要:The paper presents the fatigue test results including the cracks growth in the composite zirconium-steel subjected to oscillatory bending. Specimens of square cross-section without melted layer and with a melted layer were tested. In the specimens the net ratio of thickness of st...
作者:D. Camas , A. Lopez-Moreno
来源:[J].Fracture and Structural Integrity, 2016, Vol.10 (37), pp.114 - 123Gruppo Italiano Frattura
摘要:Most mechanical components experience multi-axial cyclic loading conditions during service. Experimental analysis of fatigue cracks under such conditions is not easy and most works tend to focus more on the simpler but less realistic case of uni-axial loading. Consequently, there...
作者:... W. Neri , P. Poulin , Nikolaos D. Alexopoulos
来源:[J].Fracture and Structural Integrity, 2017, Vol.11 (40), pp.61 - 73Gruppo Italiano Frattura
摘要:This article investigates the possibility of exploiting innovative polyvinyl alcohol fibers reinforced with carbon nanotubes (PVA-CNT fiber) as a strain sensor in cement mortars used in the restoration of Cultural Heritage Monuments. Two types of PVA-CNT fibers were embedded...
作者:Nikos G. Pnevmatikos , George A. Papagiannopoulos , George D. Hatzigeorgiou
来源:[J].Fracture and Structural Integrity, 2017, Vol.11 (40), pp.129 - 136Gruppo Italiano Frattura
摘要:An alternative design philosophy, for structures equipped with control devices, capable to resist an expected earthquake while remaining in the elastic range, is described. The idea is that a portion of the earthquake loading is undertaken by the control system and the remaining ...